Combined coatings against mechanical wear and corrosion low carbon steel
 Brožek, Vlastimil ; Pokorný, P. ; Kolísko, J. ; Vokáč, M. ; Mastný, L. ; Stoulil, J.
In this study, special ceramic coatings were prepared on low carbon steel (1.0060 - EN 10027-2) via the plasma spraying technique using a WSP®-H plasma generator with output of up to 40 kg/h of aluminum oxide. Corundum coatings were deposited directly on the surface of steel plungers equipped with an anti-corrosion interlayer of zinc phosphate. Coating adhesion properties were tested using pin-off tests (modified ISO 4624) and reached a maximum value of 26 MPa. Corrosion resistance was evaluated by measurements of impedance spectra in the 100 kHz - 10 mHz range in a water solution of sodium sulfate. The capacity of electric double-layer varied depending on the porosity and thickness of the coating. Low-porosity coatings of >1.5 mm thickness had RCT 1.29·105 Ω·m2. The abrasive resistance of coatings was measured by rotary/machining test with SiC cutting knives, using a downforce of 50 kg·cm-2. Abrasion losses decreased with the quality of finish - starting at 0.00266 g cm-2 min-1 down to virtually zero losses after polishing the surface below Ra = 0.55 micro m.
Úplný záznam

Chcete být upozorněni, pokud se objeví nové záznamy odpovídající tomuto dotazu?
Přihlásit se k odběru RSS.
Digitální repozitář :: Hledej :: Nový záznam :: Personalizace :: Nápověda
Powered by Invenio v1.1.2
Spravuje admin.invenio@techlib.cz
Tato stránka je dostupná také v následujících jazycích:
Česky  English